New technological possibility integrade LPC FineCarb® Seco/Warwick underpressure high temperature carbu-rizing technology with hardening in a Seal Quench (SQ) eg. CaseMaster® XXL. High temperature carburizing LPC in range of 1050°C (shortening the process about 40% compared with the SQ at the temp. of 950°C) with a gas cooling of the load after carburizing (perlitization) will be performed in a singlechamber vacuum furnace with gas cooling system in the range of 1.5 bar (pictured below) Heating for hardening and tempering in an oil bath quench will be performed in furnace type SQ CaseMaster® XXL mentioned above. three single-chamber furnaces VP 1500x1400x1800mm with a gross load weight of 7500kg, furnace SQ CaseMast er ® XXL 1400x1300x1800mm with a gross load weight of 7500kg.
Технические характеристики
CharacteristicsFunctiontempering, carburizing, quenchingConfigurationchamberHeat sourcegasAtmospherevacuumMaximum temperature
Max.: 1,050 °C (1,922 °F)
Min.: 950 °C (1,742 °F)