ROPE, polypropylene, black, 12mm diam., twisted

Diameter:

12mm +/- 0.5mm

Length:

30m

Weight:

1.9kg

Number of strand:

3 minimum

Type:

twisted

Material:

polypropylene, no recycled fibres, UV stabilized

Colour:

black

Tensile strength:

300kg

ROPE, polypropylene, black, 3mm diam., twisted

Diameter:

3mm +/- 0.2mm

Length:

30m

Weight:

0.1kg

Number of strand:

3 minimum

Type:

twisted

Material:

polypropylene, no recycled fibres, UV stabilized

Colour:

black

Tensile strength:

100kg

HANDSAW, for timber

Type & dimensions:

carpenter handsaw, 400-450mm blade, lacquered, overall length 550mm +/-50mm

Blade thickness:

1mm +/- 0.05mm, protected against oxidation

Blade protection:

Protective cardboard, teeth protection with hard, plastic cover.

Seal type:

laminated carbon steel, hardened and tempered

Number of teeth:

7-teeth per inch

Quality of make:

Soft edges but no dents, cracks or broken teeth

Hardness Rockwell C:

45 to 50 HRC for the whole blade, 48 to 52 HRC at teeth level

Carbon content:

0.47% to 0.55%

Manganese content:

0.5% to 0.8%

Handle:

Wooden handle, minimum 3 fixations, polished varnish hardwood, large opening 85x35mm for hand comfort when wearing gloves. Optional 45/90° square. Moisture minimum 10%, maximum 15%.

Strength testing:

With the blade inserted into a 10mm-wide slot to a depth equal to 1/3 the blade’s length, but not exceeding 150 mm, a deflection of 90° is applied 25 times in each direction without breakage or permanent set to the blade.

NAIL, FOR ROOF SHEETS, galvanized with watertight rubber washer, umbrella type

Type:

Iron nails, made of polished low-carbon steel, cold processed, not heat treated except for galvanization.

Shape:

Spiral rolled or twisted shank, sealed umbrella-type spring-head.

Corrosion treatment:

hot-dip galvanized at 300g/m2 +/-10%

Tensile strength:

minimum 650N/mm2

Accessories:

attached rubber washer with each nail

Dimensions (+/-5%):

shank: 75×3.6mm, head diameter: 20mm minimum

Rubber washer:

diameter 26mm x thickness 2mm

Packing:

packed in a strong, thick PE 130g/m² plastic bag, which can be zipped or locked

Quantity:

net weight: 0.5kg

SHOVEL, round point with Y handle

Material:

Pressed carbon-steel, hardened and tempered

Corrosion protection:

black paint

Quality of make:

no excess metal in the eye, no dents, no cracks, soft edges

Hardness Rockwell C:

35 minimum to 48 maximum HRC

Carbon content:

0.4% to 0.6%

Manganese content:

0.5% to 1%

Silicone:

0.37% maximum

Phosphorus & Sulphur:

0.06% maximum

Dimensions, full piece:

295 x 225mm +/-15mm

Hole diameter:

front side 36mm, back side 40mm, +/-5%

Weight:

1kg +/- 50g, without handle

Strength testing:

— Using a fitted, standard hardwood handle, clamp the blade of the shovel near the handle in a horizontal position. Gradually apply a load of 45kg and maintain it for 2 minutes. This should not result in any damage to the blade or a loosening of the handle, and no permanent set in excess of 25mm.

— With one centimetre of the end of the blade secured in a clamp, move the handle back and forth 30 degrees. There should be no permanent set greater than 25mm.

With the shovel held in a digging position, a 37mm in diameter piece of wood is hit hard against it. The blade should not buckle or break.

Handle:

No chips, rough surfaces, cracks, holes or knots. Smooth, polished varnish surface. Dry, strong and flexible wood. Moisture minimum 10%, maximum 15%. Handle adapted to head so that it can be blocked and secured with a nail.

Total length 1070mm +/- 50mm (head included).

The other end of the handle is made in a Y-shape with same quality of wood. The branches of the Y handle must be made of good-quality iron, securely fitted to the handle.

HOE, with long handle, large type

Material:

hot forged carbon steel, hardened and tempered, at a maximum the hardened zone should reach halfway up the back of the blade

Corrosion protection:

black paint

Quality of make:

no excess metal in the eye, no dent on the cutting edge, reinforced head with a rib from the eye to the middle of the blade length

Hardness Rockwell C:

35 minimum to 48 maximum HRC in hardened zone of the blade

Carbon content:

0.5% to 0.8%

Manganese content:

0.6% to 1.2%

Silicone:

0.37% maximum

Phosphorus & Sulphur:

0.06% maximum

Dimensions, full piece:

180 x 310 mm +/-10mm including the eye

Hole diameter:

high raised neck, front side 43 mm, back side 48 mm+/-2mm

Weight:

1.250kg +/- 150g, without handle, depending on the type of hoe

Strength testing:

— Using a fitted, standard hardwood handle, clamp the blade of the hoe near the handle in a horizontal position. Gradually apply a load of 45kg and maintain it for 2 minutes. This should not result in any damage to the blade or a loosening of the handle, and no permanent set in excess of 25mm.

— With one centimetre of the end of the blade secured in a clamp, move the handle back and forth 30 degrees. There should be no permanent set greater than 25mm.

With the hoe held in a digging position, a 37mm in diameter piece of wood is hit hard against it. The blade should not buckle or break

Handle:

No chips, rough surfaces, cracks, holes or knots. Smooth, polished varnish surface. Dry, strong, and flexible wood. Moisture minimum 10%, maximum 15%. Handle adapted to head so that it protrudes from and blocks on the other side of the head. Total length 1100mm to 1150mm.

MUTT HOE

Material:

hot forged carbon steel, hardened and tempered, at a maximum the hardened zone should reach halfway up the middle of the blade

Corrosion protection:

black paint

Quality of make:

no excess metal in the eye, no dent on the cutting edge, reinforced head with a rib from the eye to the middle of the blade length

Hardness Rockwell C: